King Hy-Pact®

Industrial Products The Super Tough Industrial Polymer Sheet King Hy-Pact is the super tough industrial polymer sheet that is environmentally stabilized with excellent physical properties. Tests have shown after 2000 hours of UV exposure King Hy-Pact outperforms both UV stabilized HDPE and Applications Abrasion and Wear Bin and Mixer Linings UHMW with superior toughness in wear resistance flexibility Chain and Belt Guides and high-impact strength. Conveyor Wear and King Hy-Pact has a clean white color with a smooth non- Guide Rails skived finish for better material flow. King Hy-Pact is produced Dock Fenders in K-Stran our advanced proprietary manufacturing process Food Processing of quality sheets with tight tolerances and custom widths Gears up to 60. Applications include but are not limited to food processing chutes star wheels fabricated parts snowplow blades and dock fenders. King Hy-Pact is the smart choice for many high abuse applications requiring superior properties Low Temp. Applications Machine Parts Material Handling outstanding flatness and a smooth surface while providing Sprockets significant cost savings compared to UHMW. Star Wheels Truck Bed Liners Specifications Standard Color Standard Sheet Size in 48 x 120 mm 1219mm x 3048mm White Custom widths up to 60 Standard Gauges in 18 mm 3.175mm Note Color accuracy can vary considerably on computer monitors and printers. Please consult your 14 6.35mm Approximate Weight 50 lbs lbs 25 lbs 22.6796kg kg 11.3398kg 38 9.525mm 75lbs 34.0194kg 12 12.7mm 34 19.05mm 1 25.4mm 99 lbs 44.9056kg 149 lbs 67.5853kg 198 lbs 89.8113kg distributor for a product sample before making critical color choices. Tolerance information Gauges 18 through 1 5 Length and width plus only at room temperature Custom sheet sizes gauges and colors available Properties Units ASTM Nominal Values Density gcc D1505 0.95 Tensile Strength Yield p.s.i. D638 4100 Elongation Yield D638 9.6 Flexural Modulus p.s.i. D790 186000 Duro

meter Shore D D2240 65 Izod Impact D256 16.6 2 Brittleness Temp. C F D746 -90C -130F Vicat Softening Temp. C F D1525 130C 266F Heat Deflection Temp. 66 p.s.i. C F D648 75C 167F Coefficient of Linear Expansion ininf D696 6.0 x 10-5 Miller Number SAR Reults SAR G75 3209 Taber Index D4060 5 King StarBoard King Hy-Pact UHMW UV Protected UV Protected UV Protected QUV Accelerated Weathering Tester Unexposed 2000 hours of exposure Unexposed 2000 hours of exposure Unexposed 2000 hours of exposure Tensile yield 70 F psi 4260 4250 4100 4100 3010 2970 Elongation yield 70 F 9.2 9.1 9.6 9.6 Tensile Break 70 F psi 690 680 1930 1440 No Break 2940 Elongation Break 70 F 160 155 260 210 No Break 3.4 Taber Index 21 45 5 12 ASTM D638 16 3.2 2 182 D638 D638 D638 D4060 IZOD notch 70 F ft lbssq in 4.1 3.9 16.6 15.7 20.02 0.84 D256 Coefficient of Friction - Kinetic 0.0888 0.0888 0.107 0.107 0.129 0.129 D1894 Coefficient of Friction - Static 0.0832 0.0832 0.102 0.102 0.102 0.102 D1894 Miler NumberSAR Results 8643.3 3209.0 453.9 G75 --- --- --- All values are determined on specimens prepared according to ASTM Standards. King HY-PACT is made entirely from FDA approved materials. Our Innovation. Your Imagination. KPC_12017_R7